white, mixing ratio of powder to water is 2:1, working life: 35-40 minutes, setting time: approx. 60 minutes, surface hardness (cured): >190 N/mm², temperature resistance (cured): short term up to 170 °C.

high quality casting powder, mixing ratio of powder to water is 4:1, working life: 8-10 minutes, curing time: approx. 30 min., expansion: 0.3%, surface hardness (cured): >300 N/mm², 1000 g powder result in 600 ml casting material, temperature resistance when cured: approx. 80 °C, very break resistant, easy releasing (from mould), weather resistant

white

weiß

white, comes in paper sack with foil insert

extraharter, hochwertiger Alphagips, kunstharzgebunden, hochweiß, feinkörnig, nicht klumpend, Mischungsverhältnis Pulver zu Wasser 3:1, Abbindezeit 8-15 Minuten, Entformzeit 30 Minuten, einfärbbar, für fortgeschrittene Anwender

harter, hochwertiger Alphagips für künstlerische Abgüsse, grobkörnig, nicht klumpend, Mischungsverhältnis Pulver zu Wasser 2,5:1, Abbindezeit 8-15 Minuten, Entformzeit 30 Minuten, bemalbar, für Anfänger und fortgeschrittene Anwender

technischer Gips für die Restaurierung, dickflüssig, stark haftend auf fast allen Materialien, auch an vertikalen Oberflächen nicht tropfend, leicht nachzuarbeiten, Mischungsverhältnis Pulver zu Wasser 2:1, Abbindezeit 10-30 Minuten, Entformzeit 60 Minuten, einfärbbar, für fortgeschrittene Anwender

two component water-based acrylic resin system (synthetic gypsum bonded with acrylic resin), for casting, laminating and coating, for interior as well as protected exterior spaces, hard (81-83 Sh-D hardness), impact resistant, odourless, material is opaque white when hardened, density (at room temperature) 1.85 g/cm³, can be coloured, mixing ratio of A to B component is 1:2.5, working life is about 8 – 10 minutes, de-moulding time is about 20 to 100 minutes, temperature resistant up to approx. 80 °C, flame retardant, self-extinguishing, shelf life with proper storage is 24 months (resin and hardener)

thickening agent for two component acrylic resin system and similar synthetic gypsums bonded with acrylic resin, thixotropic, no odour, non-toxic, mixing ratio (as percentage of weight): 1-2 % of the gypsum/acrylic mixture.

retarding agent for the two component acrylic resin system and similar synthetic gypsums bonded with acrylic resin, liquid, transparent, colourless, odourless, non-toxic, mixing ratio (as percentage of weight): 0.2 – 0.3 % of the gypsum/acrylic resin mixture.

liquid paint with high pigmentation and brilliancy for colouring the two component acrylic resin system and similar synthetic gypsums bonded with acrylic resin, non-fading, solvent-free, odourless

ready-to-use filler for interior use, drying time is 2-3 hours