Offerte
|
|
white, mixing ratio of powder to water is 2:1, working life: 35-40 minutes, setting time: approx. 60 minutes, surface hardness (cured): >190 N/mm², temperature resistance (cured): short term up to 170 °C.
putty consistency
|
|
high quality casting powder, mixing ratio of powder to water is 4:1, working life: 8-10 minutes, curing time: approx. 30 min., expansion: 0.3%, surface hardness (cured): >300 N/mm², 1000 g powder result in 600 ml casting material, temperature resistance when cured: approx. 80 °C, very break resistant, easy releasing (from ...
very smooth and firm
|
|
for hollow moulds
|
|
|
für Masken, Stützschalen für Gießformen etc.
|
|
white, comes in paper sack with foil insert
|
|
|
extraharter, hochwertiger Alphagips, kunstharzgebunden, hochweiß, feinkörnig, nicht klumpend, Mischungsverhältnis Pulver zu Wasser 3:1, Abbindezeit 8-15 Minuten, Entformzeit 30 Minuten, einfärbbar, für fortgeschrittene Anwender
hochpräzise, Härte wie Polyesterharz
|
|
|
harter, hochwertiger Alphagips für künstlerische Abgüsse, grobkörnig, nicht klumpend, Mischungsverhältnis Pulver zu Wasser 2,5:1, Abbindezeit 8-15 Minuten, Entformzeit 30 Minuten, bemalbar, für Anfänger und fortgeschrittene Anwender
Präzisionsgips, bemalbar durch offenporige Oberfläche
|
|
|
technischer Gips für die Restaurierung, dickflüssig, stark haftend auf fast allen Materialien, auch an vertikalen Oberflächen nicht tropfend, leicht nachzuarbeiten, Mischungsverhältnis Pulver zu Wasser 2:1, Abbindezeit 10-30 Minuten, Entformzeit 60 Minuten, einfärbbar, für fortgeschrittene Anwender
z.B. zum Restaurieren von Bilderrahmen und Abgüssen
|
|
two component water-based acrylic resin system (synthetic gypsum bonded with acrylic resin), for casting, laminating and coating, for interior as well as protected exterior spaces, hard (81-83 Sh-D hardness), impact resistant, odourless, material is opaque white when hardened, density (at room temperature) 1.85 g/cm³, can be ...
absolutely non-toxic – no shrinkage
|
|
thickening agent for two component acrylic resin system and similar synthetic gypsums bonded with acrylic resin, thixotropic, no odour, non-toxic, mixing ratio (as percentage of weight): 1-2 % of the gypsum/acrylic mixture.
thickens a compound (can be worked with using a spatula)
|
|
retarding agent for the two component acrylic resin system and similar synthetic gypsums bonded with acrylic resin, liquid, transparent, colourless, odourless, non-toxic, mixing ratio (as percentage of weight): 0.2 – 0.3 % of the gypsum/acrylic resin mixture.
prolongs the working time
|
|
liquid paint with high pigmentation and brilliancy for colouring the two component acrylic resin system and similar synthetic gypsums bonded with acrylic resin, non-fading, solvent-free, odourless
small amounts go a long way
|
|
ready-to-use filler for interior use, drying time is 2-3 hours
for flexible surfaces
|
|
|